EP Primer XFH is a solvent free, fast curing, two-part, 100% solids epoxy formulation providing an extremely tough finish with tenacious bond strength. This highly specialised low viscosity, fast hardening formulation ensures maximum penetration into porous surfaces, not only sealing and ‘locking’ the substrate but significantly strengthening it and helping to prevent further deterioration. EP Primer XFH also offers good chemical resistance and due to its fast curing properties, helps minimise downtime.
Typical Uses
Due to its outstanding dust-proofing and surface hardening properties, combined with its fast-curing formulation, EP Primer XFH may be used as a concrete sealer without further coating. As a universal primer, it is compatible with a wide range of Polycote epoxy topcoats and screeds. Being solvent-free, non-toxic and non-taint, EP Primer XFH is ideal for use in medical, animal, food-processing and working environments where rapid return to service is beneficial. Typical applications include warehouses, factories, workshops, laboratories and chemical bunds
Suitable substrates
EP Primer XFH has been developed specifically for concrete and cementitious substrates, but can also be used on brickwork, blockwork and timber.
Colour
EP Primer XFH is colourless and translucent.
Packaging
EP Primer XFH is supplied in pre-measured quantities as a two part 5kg unit, comprising an epoxy resin blend ‘Part A’ and hardener ‘Part B’.
Pot life @ 20°C
15 mins
Application temperature
10°C - 25°C
Initial cure time @ 20°C
6-8 hours
Curing time (recoat)
6-24 hours
Number of parts supplied
2
Primer for
Polycote Flortex product range
Coverage per 5kg unit
10-20m²
Shelf life
12 months
Storage
Store between 15-25°C. Store in a cool, dry, frost–free environment on pallets and away from walls.
Please consult the technical data sheet for full product technical data.
Preparation
Recommended methods are:
Powerfloated, loose or friable concrete – use a Vacuum Assisted Shotblaster to remove weak laitance and provide a surface key for the coating. If this is not possible, chemically etch with Polycote Etch IT then rinse thoroughly and allow to dry.
Loose paint or rust – remove, using a Vacuum Assisted Shotblaster, Floor Grinder or equivalent method.
Oil or grease – use Hot Compressed Air for large areas of contamination.
Smaller, isolated deposits may be chemically cleaned with Polycote Degrease IT then rinsed thoroughly and allowed to dry. See relevant Data Sheet prior to application.
Once prepared, the area must be kept clean and free of traffic.
Mixing
Having fully prepared the substrate, stir the individual components before mixing together.
Add the hardener to the resin and thoroughly mix for at least 4 minutes until a uniform, lump-free consistency and even colour is achieved. Make sure that any material sticking to the sides and bottom of the mixing vessel is thoroughly mixed in.
Do not hand mix or divide packs. For best results use a slow speed drill with a mixing paddle.
Ensure thorough mixing as an unmixed product will result in a poor or non-cure situation
Application
After mixing, apply immediately by brush, short to medium pile lambs wool roller or squeegee, making sure that the surface is completely covered.
Particular attention should be given to doorways and other areas of high traffic.
When finished, do not scrape the remaining contents from the container as this will invariably include unmixed raw resin.
On porous surfaces EP Primer XFH will be absorbed very quickly leaving dry patches. Apply a second coat to these dry patches to ensure good adhesion and reduce the possibility of air release from the substrate causing bubbles or pinholing in the top coat application.
Application Temperature
Normal application temperature is between 10°C and 25°C. The temperature must remain at least 3°C above the dew point until the top coat is applied, otherwise ‘blooming’ may be caused by condensation. Ensure that the ambient temperature remains above 10°C for at 24 hours after installation.