Flortex Chemical Coat

Flortex Chemical Coat is a solvent-free epoxy incorporating quality chemical-resistant fillers.
Its totally impervious gloss finish is extremely hard wearing and resists heavy forklift traffic, jet washing and all chemicals.
Flortex Chemical Coat Coverage: approx. 20 sq.m
Supplied in 5kg units (smooth) or 7kg (slip resistant)

Pot life:20-30 mins @ 20oC
Application temperature:10oC – 25oC
Initial cure time:8-12 hours
To accept traffic:24 hours
Overcoat (if required) time:within 36 hours
Full strength cure time:7 days
Full compressive strength:68N/mm²
Full tensile strength:45N/mm²
Full flexural strength:85N/mm²
Elastic modulus:2.8KN/mm²
Number of parts supplied:2
Coverage:Approx. 20 sq.m. per 5kgs unit
Primer required:Yes

Please consult the technical data sheet for full technical product data.

Preparation:Thorough substrate preparation is essential.
Prior to application of Flortex® Chemical Coat, the surface should be primed with Polycote EP Primer or WD Primer, depending on the type of substrate. Please contact Polycote Technical Helpline and prepare the surface in accordance with the appropriate primer Data Sheet.
Should the time lapse between priming and top coat exceed 48 hours, abrade the primer to ensure intercoat adhesion.

Mixing:
Having fully prepared the substrate, stir the individual components before mixing together. Add Part ‘B’ to Part ‘A’ and thoroughly mix for at least 3 minutes. For best results use a heavy duty slow speed drill with a mixing paddle.
Ensure thorough mixing as an unmixed product will result in a poor or non-cure situation.

Application:
Apply by brush, roller or squeegee, making sure that the surface is completely covered. Particular attention should be given to doorways and other areas of high traffic. When finished, DO NOT scrape the remaining contents from the container as this will invariably include unmixed resin.
Two coats are recommended in areas of high chemical aggression.
The ambient temperature of the areas should not fall below 10oC throughout the application and curing period.